High quality 7075-T7351 aluminum hexagonal rod/aluminum round rod

Product introductionProduct name:Aluminium BarGrade6063, 6061, 2024, 7075 etcRound Bar Extrudedφ10mm-φ410mmRound Bar Drawnφ1.0mm-φ10.0mmSquare & Flat Bar8mmx8mm-570mmx10mmAngle Bar8mmx8mmx1mm-280mmx40mmx4mmU Bar10mmx10mmx1mm-110mmx260mmx16mm2000 series aluminum bar:The 2000 series aluminum bar is characterize

Featured Products

Product introduction

Product name:Aluminium Bar
Grade6063, 6061, 2024, 7075 etc
Round Bar Extrudedφ10mm-φ410mm
Round Bar Drawnφ1.0mm-φ10.0mm
Square & Flat Bar8mmx8mm-570mmx10mm
Angle Bar8mmx8mmx1mm-280mmx40mmx4mm
U Bar10mmx10mmx1mm-110mmx260mmx16mm

2000 series aluminum bar:The 2000 series aluminum bar is characterized by high hardness, of which the copper element content is the highest, about 3-5%. 2000 series aluminum bar belongs to aviation aluminum material, which is not often used in conventional industry.
2024 is a typical duralumin alloy in the aluminum copper magnesium system. It is a heat treatable alloy with high strength, easy processing, easy turning and general corrosion resistance.
After heat treatment (T3, T4, t351), the mechanical properties of 2024 aluminum bar are significantly improved. The T3 state parameters are as follows: tensile strength 470mpa, 0.2% yield strength 325mpa, elongation: 10%, fatigue strength 105Mpa, hardness 120hb.
6000 series aluminum bar:6000 series aluminum bars represent 6061 and 6063, which mainly contain two elements of magnesium and silicon. Therefore, 6061 is a cold-treated aluminum forging product with the advantages of 4000 series and 5000 series. It is suitable for applications with high requirements of corrosion resistance and oxidation resistance. Good usability, easy coating, good processability.
7000 series aluminum bar:7000 series aluminum bars represent 7075 mainly containing zinc. It also belongs to Aviation series. It is aluminum magnesium zinc copper alloy. It is heat treatable alloy. It belongs to super hard aluminum alloy and has good wear resistance
High Quality 7075-T7351 Aluminum Hex Bar/Aluminum Round Bar
High Quality 7075-T7351 Aluminum Hex Bar/Aluminum Round Bar



Different Series Aluminum Alloy Bar, Aluminum Round Bar, Aluminum Solid Bar

2000 Series: 2011,2A12,2014,2017,2024
5000 Series: 5052,5652,5154,5254,5454,5056,5082,5182,5083,5086,5N01,5N02
6000 Series: 6106,6201,6011,6351,6005,6060,6061,6063,6082,6083,6463,6262
7000 Series: 7003,7005,7020,7050,7075,7A04


Different Treatment:
1. O Condition.
2. H Condition: H111/H112/H113/H13.
3. T Condition: T3/T351/T4/T5/T6/T651/T6511/T73/T7351/T7651/T76511.


2011/2A12/2014/2017/2024 Aluminum Alloy Bar Aluminum Round Bar

2024 aluminum bar, aluminum rod is a typical hard aluminum alloy in the aluminum-copper-magnesium series. Its composition is reasonable and its comprehensive performance is good. This alloy is produced in many countries and is the largest amount of hard aluminum.

The alloy can be used as working parts below 150 ° C. The strength of 2024 alloy is higher than that of 7075 alloy. The forming performance is better in the hot state, annealing and new quenching states, and the heat treatment strengthening effect is significant, but the heat treatment process is strict. Poor corrosion resistance, but covered with pure aluminum can be effectively protected; cracks are easy to occur during welding, but special processes can be used for welding and riveting.

2024 aluminum bar,aluminum rod is a high-strength hard aluminum, which can be strengthened by heat treatment. It has moderate plasticity in the quenched and freshly quenched state. It has good spot welding and has the tendency to form intergranular cracks when gas welding. The cutting performance is good, and the machinability after annealing is low: the corrosion resistance is not high. Anodizing treatment and painting methods are often used or the surface is coated with an aluminum layer to improve its corrosion resistance.

2024 is mainly used to make various high-load parts and components (but not including stamping parts and forgings) such as skeleton parts, skins, bulkheads, ribs, spar, rivets and other working parts below 150 ºC on aircraft.

Chemical Composition
 
AlloySiFeCuMnMgCrZnTiAl
20240.50.53.8-4.90.3-0.91.2-1.80.100.250.15remain

Mechanical Properties
 
Aluminum Alloy & TemperatureTensile Strength
(Rm/MPa)
Proof Strength
(Rp0.20/Mpa)
Percentage Elongation
(%)
Hardness
(HB)
202447032510120


5052/5083/5005/5A05 Good Corrosion Resistance and Weldability Aluminum Bar Aluminum Alloy Bar

5052 aluminum alloy is a kind of Al Mg alloy, which is widely used, especially in the construction industry. It is the most promising alloy. It has good corrosion resistance, weldability, cold workability and medium strength. The main alloy element of 5052 aluminum alloy is magnesium, which has good forming and processing performance, corrosion resistance, weldability and medium strength. It is used to manufacture aircraft oil tank, oil pipe, as well as sheet metal parts of traffic vehicles and ships, instruments, street lamp bracket and rivets, hardware products, electric appliance outer shell, etc.

5052 aluminum alloy is the most widely used antirust aluminum, which has high strength, especially fatigue strength: high plasticity and corrosion resistance, can not be strengthened by heat treatment, good plasticity in semi cold work hardening, low plasticity in cold work hardening, good corrosion resistance, good weldability, poor machinability and polishing. It is mainly used for low load parts that require high plasticity and good weldability and work in liquid or gas medium, such as oil tank, gasoline or lubricating oil conduit, various liquid containers and other small load parts made by deep drawing: wire rod is used for rivets.

Chemical Composition

Aluminum al: margin
Silicon Si: ≤ 0.25
Copper Cu: ≤ 0.10
Mg: 2.2 ~ 2.8
Zinc Zn: ≤ 0.10
Manganese Mn: ≤ 0.10
Cr: 0.15-0.35
Iron Fe: ≤ 0.40
Note: single: < 0.05; total: < 0.15
 
AlloySiFeCuMnMgCrZnSingleOther
5052≤0.25≤0.4≤0.10≤0.102.2-2.80.15-0.30≤0.10≤0.05≤0.15

Aluminum Bar: Diameter φ8 - φ460. Length: 1~6 meters.

Aluminum Tube: (diameter φ10 - φ460, wall thickness 0.3-40mm)
Pure aluminum tube, alloy aluminum tube, seamless aluminum tube (extrusion, drawing), large diameter aluminum tube, thick wall aluminum tube, alumina tube, aluminum flat tube, aluminum square tube, elliptical tube, coil, fine pull Pull out the aluminum tube.

Technical Parameter
Alloy TypeTensile Strength
(250ºC/MPa)
0.2% Yield Strength
(MPa)
Hardness
(HB)
Elongation rate
(%)
5052-H1121751956012
5083-H1121802116514
6061-T6512902409512
6082-T6513152809412
7050-T65151045513510
7075-T65157250315011
2024-T35147032512020

6060/6061/6063/6082/6083 T351/T4/T5/T6/T651/T6511 Aluminum Alloy Bar Aluminum Round Bar

6063 series aluminum bar, aluminum rod, aluminum alloy bar, aluminum alloy rod by the company is a low-alloyed Al-Mg-Si high-plastic alloy. It has many valuable features as follows:

1.Heat treatment strengthening, high impact toughness.

2.There is excellent thermoplasticity, which can be kneaded at high speed into a messy layout, various profiles of thin-walled hollow or forged forgings with complicated layout, wide quenching temperature, low quenching sensitivity, kneading and casting after demoulding only The temperature is required to be higher than the quenching temperature. That is, it can be quenched by spraying water or water. Thin-walled parts (6<3mm) are also capable of wind quenching.

3.The welding function and corrosion resistance are excellent, and there is no stress corrosion cracking tendency. In the heat-treated reinforced aluminum alloy, the Al-Mg-Si alloy is an alloy in which only the stress corrosion cracking appearance is not found. Fourth, the appearance after processing is very bright, and simple anodizing and coloring.

Chemical Composition
 
AlloySiFeCuMnMgCrZnTiOtherAl
60630.20-0.600.350.10.150.60-0.900.050.150.10.050.15remain
 
AlloySiFeCuMnMgCrZnTiOtherAl
60610.4-0.80.70.15~0.40.150.8-1.20.04~0.350.250.150.050.15remain

Mechanical Properties
 
Aluminum Alloy & TemperatureTensile Strength
(Rm/MPa)
Proof Strength
(Rp0.20/Mpa)
Percentage Elongation
After Fracture
(A/%)

Hardness
(HB)
6063-T6/T651≥230≥110≥8≥70
 
Aluminum Alloy & TemperatureTensile Strength
(Rm/MPa)
Proof Strength
(Rp0.20/Mpa)
Percentage Elongation
After Fracture
(A/%)

Hardness
(HB)
6061-T6/T651≥260≥1806~9≥95

High Quality 7075-T7351 Aluminum Hex Bar/Aluminum Round Bar
High Quality 7075-T7351 Aluminum Hex Bar/Aluminum Round Bar


Company Introduction:


Hebei Enmin metal material import and Export Co., Ltd.
Our company,  is located in XingtaiCity, Hebei Province,China.The building area of our factory is more than 2000 square meters, with all kinds of Metallic materials.
We are a professional manufacturer of zinc ingot,lead ingot,aluminum ingot, magnesium ingot,aluminum alloy ingot ,aluminum alloy bar ,silicon manganese alloy,wolfram-cobalt hard alloy,copper wire scrap,nickel sheet metal scrap,cobalt powder,  nickel powder and  other metal products.
Hebei Enmin Metal Material Import and Export Co. , Ltd. always adhere to the "quality first, customer first, credit first" business philosophy and "exceed customer expectations, Develop Team Spirit, assume social responsibility" corporate values: efforts to meet the potential needs of customers. Through the unremitting efforts of all the staff, we have made remarkable achievements. Now we have entered into cooperation with customers in many countries. As a company committed to World Trade Cooperation, the company's main products include copper, aluminum, zinc,  , magnesium and other products, a full range of products to meet the needs of customers in many ways. 
High Quality 7075-T7351 Aluminum Hex Bar/Aluminum Round Bar



 

Contact us

Please feel free to give your inquiry in the form below We will reply you in 24 hours